پديد آورنده :
عابدي، حسين
عنوان :
بررسي ميزان برجستگي نخ و خواص مكانيكي پارچه هاي بافته شده از نخهاي پلي استرفيلامنتي تابدار
مقطع تحصيلي :
كارشناسي ارشد
گرايش تحصيلي :
تكنولوژي نساجي
محل تحصيل :
اصفهان: دانشگاه صنعتي اصفهان، دانشكده نساجي
صفحه شمار :
يازده،106ص.: مصور،جدول،نمودار
يادداشت :
ص.ع.به فارسي و انگليسي
توصيفگر ها :
برجستگي سطحي , خواص خمشي , خواص كششي
تاريخ نمايه سازي :
27/9/92
استاد داور :
محمدذره بيني، محمد شيخ زاده
چكيده فارسي :
به فارسي و انگليسي: قابل رويت در نسخه ديجيتالي
چكيده انگليسي :
Investigation on the Protrusion and Mechanical Properties of Woven Fabric Consist of High Twist Filament Polyester Yarn Hosein Abedi habedi89@yahoo com Date of Submission September 22 2013 Department of Textile Engineering Isfahan University of Technology Isfahan 84156 83111 Iran Degree M Sc Language Farsi Superviser Mohammad Ghane m ghane@cc iut ac ir Abstract Some properties of Polyester fabrics are more desirable in comparison with other apparel fabrics These properties include high strength long aging time high flexibility low expenses etc In order to obtain the optimum superficial and sensory properties like better handling un sliding effect appropriate optical properties better drape it would be necessary to evaluate some surface and mechanical properties The main aim of this work was to optimize the polyester fabric characterization using the surface and mechanical properties In order to do this twenty of polyester fabrics were prepared High twist filament yarns were used in weaving the samples Four different wave patterns with five weft density were selected as independent variables For each fabric type three various test groups including surface protrusion using image processing technique bending properties and tensile properties in weft warp and bias direction were performed Statistical results showed that weft density and wave pattern have significant effect on surface protrusion bending and tensile properties The results of the tensile tests showed that for all wave patterns the resiliency and linearity of the fabrics in biased direction are much less in comparison to weft and warp directions Keywords polyester fabrics surface protrusion bending and tensile properties PDF created with pdfFactory trial version www pdffactory com
استاد داور :
محمدذره بيني، محمد شيخ زاده